"Fergus Kyle" <fkyle@bigwave.ca> Subject: Re: My
email on metal treatment Date: Sat, 20 Sep 97 17:48:58 GMT
Graham:
Thanks for your reply...... as for knowing more, well, that ain't so, altho'
I've done a bit of looking into the various treatments.
----------
> No your deod isn't faulty, it just looked as though you know more about it
> than me.
> Why not hard anodise?
Ivan advises (I think rightly) that the current belief is that Hard anodising
actually creates a shell which is liable to cracking. It'sd OK for some
surfaces
where vibration is not a considerati
>Sealed, hot water or dichromate is supposed to
> restore fatigue strength I understand. But, does it also prevent bonding. I
> don't like scuff sanding anodised parts, good way to reduce fatigue
> strength one might think.
> Graham
I agree, but my guru here tells me that zinc dichromate bonds well, so that
was part of the reason for my message. I will be anodising on Monday, but am
holding
off on the zinc dichromate treatmen Thanks again for the reply.
Ferg____
>
|